Allotropes | silvery-white, β (beta); gray, α (alpha) |
---|
Appearance | silvery-white (beta, β) or gray (alpha, α) |
---|
|
|
| 118.710(7)[1] |
---|
|
|
|
Group | group 14 (carbon group) |
---|
Period | period 5 |
---|
Block | p-block |
---|
Electron configuration | [Kr] 4d10 5s2 5p2 |
---|
Electrons per shell | 2, 8, 18, 18, 4 |
---|
|
Phase at STP | solid |
---|
Melting point | 505.08 K (231.93 °C, 449.47 °F) |
---|
Boiling point | 2875 K (2602 °C, 4716 °F) |
---|
Density (near r.t.) | white, β: 7.265 g/cm3 gray, α: 5.769 g/cm3 |
---|
when liquid (at m.p.) | 6.99 g/cm3 |
---|
Heat of fusion | white, β: 7.03 kJ/mol |
---|
Heat of vaporization | white, β: 296.1 kJ/mol |
---|
Molar heat capacity | white, β: 27.112 J/(mol·K) |
---|
Vapor pressure
P (Pa) |
1 |
10 |
100 |
1 k |
10 k |
100 k |
at T (K) |
1497 |
1657 |
1855 |
2107 |
2438 |
2893 |
|
|
Oxidation states | −4, −3, −2, −1, 0,[2] +1,[3] +2, +3,[4] +4 (an amphoteric oxide) |
---|
Electronegativity | Pauling scale: 1.96 |
---|
Ionization energies | - 1st: 708.6 kJ/mol
- 2nd: 1411.8 kJ/mol
- 3rd: 2943.0 kJ/mol
-
|
---|
Atomic radius | empirical: 140 pm |
---|
Covalent radius | 139±4 pm |
---|
Van der Waals radius | 217 pm |
---|
Spectral lines of tin |
|
Natural occurrence | primordial |
---|
Crystal structure | tetragonal white (β) |
---|
Crystal structure | face-centered diamond-cubic gray (α) |
---|
Speed of sound thin rod | 2730 m/s (at r.t.) (rolled) |
---|
Thermal expansion | 22.0 µm/(m⋅K) (at 25 °C) |
---|
Thermal conductivity | 66.8 W/(m⋅K) |
---|
Electrical resistivity | 115 nΩ⋅m (at 0 °C) |
---|
Magnetic ordering | gray: diamagnetic[5] white (β): paramagnetic |
---|
Molar magnetic susceptibility | (white) +3.1·10−6 cm3/mol (298 K)[6] |
---|
Young's modulus | 50 GPa |
---|
Shear modulus | 18 GPa |
---|
Bulk modulus | 58 GPa |
---|
Poisson ratio | 0.36 |
---|
Brinell hardness | 50–440 MPa |
---|
CAS Number | 7440-31-5 |
---|
|
Discovery | around 3500 BC |
---|
Symbol | "Sn": from Latin stannum |
---|
|
|
Main isotopes[7] |
Decay |
|
abundance |
half-life (t1/2) |
mode |
product |
112Sn |
0.970% |
stable |
114Sn |
0.66% |
stable |
115Sn |
0.34% |
stable |
116Sn |
14.5% |
stable |
117Sn |
7.68% |
stable |
118Sn |
24.2% |
stable |
119Sn |
8.59% |
stable |
120Sn |
32.6% |
stable |
122Sn |
4.63% |
stable |
124Sn |
5.79% |
stable |
126Sn |
trace |
2.3×105 y |
β− |
126Sb |
|
|
Category: Tin | references |