Titanium |
---|
Pronunciation | |
---|
Appearance | sillery gray-white metallic |
---|
Standard atomic weight Ar, std(Ti) | 7001478670000000000♠47.867(1)[2] |
---|
Titanium in the periodic cairt |
---|
|
– ↑ Ti ↓ Zr |
scandium ← titanium → vanadium |
|
|
Atomic nummer (Z) | 22 |
---|
Group | group 4 |
---|
Period | period 4 |
---|
Block | d-block |
---|
Element category | Transeetion metal |
---|
Electron confeeguration | [Ar] 3d2 4s2 |
---|
Electrons per shell | 2, 8, 10, 2 |
---|
Pheesical properties |
---|
Phase at STP | solit |
---|
Meltin pynt | 1941 K (1668 °C, 3034 °F) |
---|
Bylin pynt | 3560 K (3287 °C, 5949 °F) |
---|
Density (near r.t.) | 4.506 g/cm3 |
---|
when liquid (at m.p.) | 4.11 g/cm3 |
---|
Heat o fusion | 14.15 kJ/mol |
---|
Heat o vapourisation | 425 kJ/mol |
---|
Molar heat capacity | 25.060 J/(mol·K) |
---|
Vapour pressur
P (Pa) |
1 |
10 |
100 |
1 k |
10 k |
100 k |
at T (K) |
1982 |
2171 |
(2403) |
2692 |
3064 |
3558 |
|
Atomic properties |
---|
Oxidation states | −2, −1, 0,[3] +1, +2, +3, +4[4] (an amphoteric oxide) |
---|
Electronegativity | Pauling scale: 1.54 |
---|
Ionisation energies | - 1st: 658.8 kJ/mol
- 2nd: 1309.8 kJ/mol
- 3rd: 2652.5 kJ/mol
- (more)
|
---|
Atomic radius | empirical: 147 pm |
---|
Covalent radius | 160±8 pm |
---|
Spectral lines o titanium |
Ither properties |
---|
Naitural occurrence | primordial |
---|
Creestal structur | hexagonal close-packed (hcp) |
---|
Speed o soond thin rod | 5090 m/s (at r.t.) |
---|
Thermal expansion | 8.6 µm/(m·K) (at 25 °C) |
---|
Thermal conductivity | 21.9 W/(m·K) |
---|
Electrical resistivity | 420 nΩ·m (at 20 °C) |
---|
Magnetic orderin | paramagnetic |
---|
Magnetic susceptibility | +153.0·10−6 cm3/mol (293 K)[5] |
---|
Young's modulus | 116 GPa |
---|
Shear modulus | 44 GPa |
---|
Bulk modulus | 110 GPa |
---|
Poisson ratio | 0.32 |
---|
Mohs haurdness | 6.0 |
---|
Vickers haurdness | 830–3420 MPa |
---|
Brinell haurdness | 716–2770 MPa |
---|
CAS Nummer | 7440-32-6 |
---|
History |
---|
Diskivery | William Gregor (1791) |
---|
First isolation | Jöns Jakob Berzelius (1825) |
---|
Named by | Martin Heinrich Klaproth (1795) |
---|
Main isotopes o titanium |
---|
Isotope |
Abundance |
Hauf-life (t1/2) |
Decay mode |
Product |
44Ti |
syn |
63 y |
ε |
44Sc |
γ |
– |
46Ti |
8.25% |
stable |
47Ti |
7.44% |
stable |
48Ti |
73.72% |
stable |
49Ti |
5.41% |
stable |
50Ti |
5.18% |
stable |
|
| references |