Iridium |
---|
Pronunciation | (ih-RID-ee-əm) |
---|
Appearance | sillery white |
---|
Standard atomic weight Ar, std(Ir) | 7002192217000000000♠192.217(2)[1] |
---|
Iridium in the periodic cairt |
---|
|
Atomic nummer (Z) | 77 |
---|
Group | group 9 |
---|
Period | period 6 |
---|
Block | d-block |
---|
Element category | Transeetion metal |
---|
Electron confeeguration | [Xe] 4f14 5d7 6s2 |
---|
Electrons per shell | 2, 8, 18, 32, 15, 2 |
---|
Pheesical properties |
---|
Phase at STP | solid |
---|
Meltin pynt | 2719 K (2446 °C, 4435 °F) |
---|
Bylin pynt | 4403 K (4130 °C, 7466 °F) |
---|
Density (near r.t.) | 22.56 g/cm3 |
---|
when liquid (at m.p.) | 19 g/cm3 |
---|
Heat o fusion | 41.12 kJ/mol |
---|
Heat o vapourisation | 564 kJ/mol |
---|
Molar heat capacity | 25.10 J/(mol·K) |
---|
Vapour pressur
P (Pa) |
1 |
10 |
100 |
1 k |
10 k |
100 k |
at T (K) |
2713 |
2957 |
3252 |
3614 |
4069 |
4659 |
|
Atomic properties |
---|
Oxidation states | −3, −1, 0, +1, +2, +3, +4, +5, +6, +7, +8, +9[2] |
---|
Electronegativity | Pauling scale: 2.20 |
---|
Ionisation energies | - 1st: 880 kJ/mol
- 2nd: 1600 kJ/mol
-
|
---|
Atomic radius | empirical: 136 pm |
---|
Covalent radius | 141±6 pm |
---|
Spectral lines o iridium |
Ither properties |
---|
Naitural occurrence | primordial |
---|
Creestal structur | face-centred cubic |
---|
Speed o soond thin rod | 4825 m/s (at 20 °C) |
---|
Thermal expansion | 6.4 µm/(m·K) |
---|
Thermal conductivity | 147 W/(m·K) |
---|
Electrical resistivity | 47.1 nΩ·m (at 20 °C) |
---|
Magnetic orderin | paramagnetic[3] |
---|
Magnetic susceptibility | +25.6·10−6 cm3/mol (298 K)[4] |
---|
Young's modulus | 528 GPa |
---|
Shear modulus | 210 GPa |
---|
Bulk modulus | 320 GPa |
---|
Poisson ratio | 0.26 |
---|
Mohs haurdness | 6.5 |
---|
Vickers haurdness | 1760–2200 MPa |
---|
Brinell haurdness | 1670 MPa |
---|
CAS Nummer | 7439-88-5 |
---|
History |
---|
Diskivery an first isolation | Smithson Tennant (1803) |
---|
Main isotopes o iridium |
---|
Isotope |
Abundance |
Hauf-life (t1/2) |
Decay mode |
Product |
188Ir |
syn |
1.73 d |
ε |
188Os |
189Ir |
syn |
13.2 d |
ε |
189Os |
190Ir |
syn |
11.8 d |
ε |
190Os |
191Ir |
37.3% |
stable |
192Ir |
syn |
73.827 d |
β− |
192Pt |
ε |
192Os |
192m2Ir |
syn |
241 y |
IT |
192Ir |
193Ir |
62.7% |
stable |
193mIr |
syn |
10.5 d |
IT |
193Ir |
194Ir |
syn |
19.3 h |
β− |
194Pt |
194m2Ir |
syn |
171 d |
IT |
194Ir |
|
| references |